WAX YOUR THREAD, CONDITION IT, OR DON’T

Posted by learntobead on June 4, 2013

WAX YOUR THREAD, CONDITION IT, OR DON’T

microcrystalline-wax

We are always debating here whether to wax your thread or not, and if so, what wax or thread conditioner to use.

I have some strong opinions about this.

How about you?

Some people never wax.
Some people think it makes no difference as to whether the thread breaks.
Some people think it ruins the beads.

sun1mornbeeswax

By the way, my opinions:
With beading thread, like Nymo or C-Lon, always wax.
Always use microcrystalline wax
Never use Thread Heaven.

With cable threads, like FireLine, sometimes wax.
I wax when the stitch I am doing is a loose one, like Ndebele or Right Angle Weave. The stickiness of the wax helps me maintain a tight thread tension.

Never use pre-waxed thread like Silamide.
Silamide is not abrasion-resistant, so it breaks too easily with beads. The holes of most beads are pretty sharp.

Waxing keeps the beading thread from fraying.
It’s stickiness allows greater control over managing thread tension.
The process of waxing stretches the thread a bit before you use it.
The waxy buildup helps fill in the jagged rim of the holes of your beads, making them a little less likely to cut into your stringing material.